RESUMO
AA6111 aluminum automotive body-sheet alloy has been formulated from 100% Taint Tabor scrap aluminum. Direct chill casting with and without high shear melt conditioning (HSMC) was used to produce the AA6111 alloy billets. Both homogenized and non-homogenized billets were extruded into sheets. The optical micrographs of the melt conditioned direct chill (MC-DC) samples showed refined equiaxed grains in comparison to direct chill (DC) cast and direct chill grain refined (DC-GR) samples. Optical metallography showed extensive peripheral coarse grain (PCG) for the DC, DC-GR and MC-DC planks extruded from the homogenized standard AA6111 billets while planks extruded from modified AA6111 billets (with recrystallization inhibitors) showed thin PCG band. The co-addition of recrystallization inhibitors Mn, Zr, and Cr with elimination of the billet homogenization step had a favorable impact on the microstructure of the AA6111 alloy following the extrusion process where a fibrous grain structure was retained across the whole section of the planks. The mechanical properties of as-cast planks extruded from non-homogenized billets were similar to those extruded from homogenized billets. Eliminating the homogenization heat treatment step prior to extrusion has important ramifications in terms of processing cost reduction.
RESUMO
The melt conditioned direct chill (MC-DC) casting process has been used to produce billets and extruded planks of AA5754 alloy formulated from 100% recycled Taint Tabor scrap aluminum. The billets were homogenized and then extruded into flat planks. Optical metallography of the MC-DC cast billets showed equiaxed refined grains in comparison to conventional direct chill (DC) cast and direct chill grain refined (DC-GR) cast billets formulated from the same Taint Tabor scrap. Microstructural evaluation of the extruded planks showed extensive peripheral coarse grain (PCG) for the DC, DC-GR and MC-DC cast planks. The 2 mm and 1 mm MC-DC cast planks produced after cold rolling and heat treatment showed a fully recrystallized microstructure at 380 °C and 300 °C for 10 min respectively with an improvement in mechanical properties over DC-GR cast and similarly processed planks. The as-extruded MC-DC cast planks tensile tested in the transverse direction showed 34% elongation and 213 MPa ultimate tensile strength. These tensile results showed 5.8% higher elongation and 1.2% higher ultimate tensile strength compared with the DC-GR planks after applying high shear melt conditioning.
RESUMO
Casting is the first step toward the production of majority of metal products whether the final processing step is casting or other thermomechanical processes such as extrusion or forging. The high shear melt conditioning provides an easily adopted pathway to producing castings with a more uniform fine-grained microstructure along with a more uniform distribution of the chemical composition leading to fewer defects as a result of reduced shrinkage porosities and the presence of large oxide films through the microstructure. The effectiveness of high shear melt conditioning in improving the microstructure of processes used in industry illustrates the versatility of the high shear melt conditioning technology. The application of high shear process to direct chill and twin roll casting process is demonstrated with examples from magnesium melts.